采用熔化极气体保护焊(GMAW)对WDB620D钢进行了焊接工艺评定,对其焊缝进行了NDT无损检测,并对焊接接头进行了拉伸、弯曲、冲击等力学性能试验。试验结果表明,焊接工艺评定的各项力学性能和焊接性能指标都达到了图纸设计和ASMEⅨ标准的各项要求,该GMAW工艺在丰宁抽水蓄能电站的蜗壳制造中进行了应用和验证,并取得了良好的效果。
Welding procedure qualification of WDB620D steel was evaluated by gas metal arc welding(GMAW).Non-destructive testing was carried out on welds of WDB620D steel,and mechanical properties tests of tensile,bending and impact were carried out on welded joints.Test results showed that mechanical properties and weldability indexes of welding procedure qualification met requirements of drawings and ASMEⅨstandard.GMAW process was applied and verified in the volutes manufacturing of Fengning Pumped Storage Power Station,and good results were obtained.
作者
李明伟
雷进波
于莉莉
吴建忠
周长安
Li Mingwei;Lei Jinbo;Yu Lili;Wu Jianzhong;Zhou Changan(Hangzhou Hongchen Energy Technology Co.,Ltd.,Hangzhou 310063,China;Zhejiang Axiang New Energy Equipment Co.,LTD.,Huzhou 313000,Zhejiang,China)
出处
《焊接》
2024年第3期76-80,共5页
Welding & Joining
关键词
WDB620D
焊接工艺评定
热影响区
蜗壳制造
WDB620D
welding procedure qualification
heat affected zone
spiral case manufacturing