摘要
A new Ni+Zr co-alloyed FeCrAl-ODS(oxide-dispersion-strengthened)ferritic alloy was fabricated by ball-milling and hot-isostatic-pressing.Using electron microscopy and atom probe tomography,the dispersive formation of high density core-shelled nano-particles of various sizes was confirmed with a common B2-NiAl shell.Among which,median-sized nano-particles(20-50 nm)typically have an Y_(4)Al_(2)O_(9)nano-core of<~20 nm,ultra-fine nano-particles(<~20)nm have an Y_(4)Zr_(3)O_(12)nano-core of<~10 nm,and larger-sized nano-particles(50-100 nm)incorporate an ultra-fine Y_(4)Al_(2)O_(9)nano-core and a few ultra-fine Y_(4)Zr_(3)O_(12)nano-oxides.All these nano-phases were highly coherent with the ferritic matrix.No large Y--Al-O nano-oxides were formed.The total number density of ultra-fine nano-particles was estimated as~2×10^(23)m^(-3)with a mean size of 6.3 nm only,and accordingly,the new alloy achieved an excellent combination of strength and ductility at high temperatures.
基金
This work was financially supported by the National MCF Energy R&D Program of China(No.2018YFE0306100).The computational resources at Hefei Advanced Computing Center and the High Performance Computing Center of Central South University are also highly appreciated.