摘要
以桥联茂金属催化剂催化丙烯与乙烯共聚合,探究了助催化剂、反应温度、共聚单体用量、n(Al)∶n(Zr)和n(B)∶n(Zr)等对丙烯与乙烯共聚合及聚合物结构与性能的影响,优化了间歇溶液聚合的工艺参数,制备了丙烯-乙烯无规共聚物。在合适条件下,该催化体系的活性最高达2.05×10^(7)g/(mol·h)。溶液聚合小试最佳工艺条件:反应温度为70℃,n(Al)∶n(Zr)=150,n(B)∶n(Zr)=1.5。
Bridged metallocene catalyst was used as the main catalyst to explore the effects of process conditions such as cocatalysts,polymerization temperature,comonomer concentration,n(Al)∶n(Zr)and n(B)∶n(Zr)on propylene-ethylene copolymerization and polymer structure and properties.The process parameters of intermittent solution polymerization were optimized to prepare propylene-ethylene random copolymer with the highest activity of 2.05×10^(7)g/(mol·h).The optimal process conditions of solution polymerization are as follows:the temperature is 70℃,n(Al)∶n(Zr)=150,n(B)∶n(Zr)=1.5.
作者
王国栋
方园园
宋文波
Wang Guodong;Fang Yuanyuan;Song Wenbo(SINOPEC(Beijing)Research Institute of Chemical Industry Co.,Ltd.,Beijing 100013,China)
出处
《合成树脂及塑料》
CAS
北大核心
2024年第2期7-10,15,共5页
China Synthetic Resin and Plastics
关键词
茂金属催化剂
丙烯
乙烯
共聚合
丙烯基弹性体
metallocene catalyst
propylene
ethylene
copolymerization
propylene-based elastomer