Carrageenan Fiber Prepared by a New Process Route of Ba^(2+)Ion Pre-Crosslinking in the Spinning Solution

Ba^(2+)pre-crosslinked carrageenan fiber(Ba/CAF)was prepared by adding a small amount of Ba^(2+) to the carrageenan(CA)solution as the spinning solution.Ba/CAF-n/A,Ba/CAF-n/B and Ba/CAF-n/C were prepared with ethanol solution(combine A),high concentration BaCl_(2)solution(combine B)and low concentration BaCl_(2)solution(combine C),as coagulation bath and stretch bath,respectively.The combination of coagulation bath and stretch bath suitable for Ba^(2+) pre-crosslinking wet spinning was screened.The results showed that Ba^(2+) can induce the birefringence of the CA molecular chain,and the Ba^(2+) pre-crosslinking effect is the best when the CA mass fraction is 8.0 wt%.From the perspective of production safety,fiber performance and spinning cost,the coagulation bath of 3.5 wt%BaCl_(2)solution and stretch bath of 1.7 wt%BaCl_(2)solution,that is,combination C with low concentration BaCl_(2)solution,is the best choice.Ba/CAF-8.0/C was obtained under the best conditions.The linear intensity,water absorption and flame retardancy study showed that the breaking strength of Ba/CAF-8.0/C is as high as 1.61 cN/dtex,the water absorption was 649.2%and 574.3%,in deionized water and normal saline,respectively,and the LOI value reached 32.