摘要
The integration of lightweight and high-modulus magnesium-based materials is becoming increasingly valued as structural materials due to the complexity and intelligence of industrial products like automobiles and electronics.In this study,the graphene nanoplatelets(GNPs)/Mg-Zn-Zr composites with 0.5 wt%GNPs were successfully prepared by the combination of multidirectional forging(MDF)and hot extrusion(Ex).The newly-developed composites after multi-step deformation possessed excellent strength and modulus,with a tensile strength exceeding 375 MPa and an elastic modulus reaching 54 GPa.The results revealed that the stripping and thinning of GNPs bands parallel to the extrusion direction occurred after MDF+Ex,which promoted the dynamic recrystallization and the formation of numerous fine grains.The significant improvement in comprehensive mechanical performances of the composites could be primarily ascribed to the refinement of grain size caused by the optimized distribution of GNPs,and efficient load transfer facilitated by the tight interface.
基金
supported by the Fundamental Research Program of Shanxi Province (Grant Nos.202203021221088 and 202103021223043)
the Fund Program for the Scientific Activities of Selected Returned Overseas Professionals in Shanxi Province (Grant No.20230010)
the Shanxi Provincial Science and Technology Major Special Project plan of"Taking the lead in unveiling the list" (Grant No.202201050201012)
the Research Project Supported by Shanxi Scholarship Council of China (Grant No.2023-063)
the National Natural Science Foundation of China (Grant Nos.51771129,52271109 and 51771128)
the National Key Research and Development Program for Young Scientists (Grant No.2021YFB3703300)
the Special Fund Project for Guiding Local Science and Technology Development by the Central Government (Grant No.YDZJSX2021B019)
the Open Foundation of State Key Laboratory of Compressor Technology (Compressor Technology Laboratory of Anhui Province) (Grant No.SKL-YSJ202103).