摘要
This study explores how the chemical interaction between magnesium hydride(MgH_(2))and the additive CrO_(3) influences the hydrogen/lithium storage characteristics of MgH_(2).We have observed that a 5 wt.%CrO_(3) additive reduces the dehydrogenation activation energy of MgH_(2) by 68 kJ/mol and lowers the required dehydrogenation temperature by 80℃.CrO_(3) added MgH_(2) was also tested as an anode in an Li ion battery,and it is possible to deliver over 90%of the total theoretical capacity(2038 mAh/g).Evidence for improved reversibility in the battery reaction is found only after the incorporation of additives with MgH_(2).In depth characterization study by X-ray diffraction(XRD)technique provides convincing evidence that the CrO_(3) additive interacts with MgH_(2) and produces Cr/MgO byproducts.Gibbs free energy analyses confirm the thermodynamic feasibility of conversion from MgH_(2)/CrO_(3) to MgO/Cr,which is well supported by the identification of Cr(0)in the powder by X ray photoelectron spectroscopy(XPS)technique.Through high resolution transmission electron microscopy(HRTEM)and energy dispersive spectroscopy(EDS)we found evidence for the presence of 5 nm size Cr nanocrystals on the surface of MgO rock salt nanoparticles.There is also convincing ground to consider that MgO rock salt accommodates Cr in the lattice.These observations support the argument that creation of active metal–metal dissolved rock salt oxide interface may be vital for improving the reactivity of MgH_(2),both for the improved storage of hydrogen and lithium.
基金
supported by the projects UIDB/00481/2020 and UIDP/00481/2020-Fundação para a Ciência e a Tecnologia,DOI 10.54499/UIDB/00481/2020(https://doi.org/10.54499/UIDB/00481/2020)and DOI 10.54499/UIDP/00481/2020(https://doi.org/10.54499/UIDP/00481/2020)
supported by CENTRO-01-0145-FEDER-022083-Centro Portugal Regional Operational Programme(Centro 2020),under the PORTUGAL 2020 Partnership Agreement,through the European Regional Development Fund(ERDF).This article is a result of the Innovation Pact“NGS-New Generation Storage”(C644936001-00000045)
by“NGS”Consortium,co-financed by NextGeneration EU,through the Incentive System“Agendas para a Inovação Empresarial”(“Agendas for Business Innovation”)
within the Recovery and Resilience Plan(PRR).D.P acknowledges FCT,Portugal for the financial support with reference CEECIND/04158/2017(https://doi.org/10.54499/CEECIND/04158/2017/CP1459/CT0029)
funding from the SMART-ER project,funded by the European Union’s Horizon 2020 research and innovation programme under Grant Agreement#101016888.
support granted by the Recovery and Resilience Plan(PRR)and by the Next Generation EU European Funds to Universidade de Aveiro,through the Agenda for Business Innovation“NGS-Next Generation Storage”(Project no 02/C05-i01.01/2022 with the application C644936001-00000045).