As an important A_(2)B_(2)O_(7)-type ceramic,(La_(0.2)Nd_(0.2)Sm_(0.2)Gd_(0.2)Eu_(0.2))_(2)Zr_(2)O_(7)high-entropy pyrochlore pos-sesses promising properties such as high melting point,high chemical durability,and low thermal conductivity.However,the low sintering ability limits its application in thermal barrier coating and radioactive waste immobilization.It usually needs long-term high-temperature soaking to achieve full density,but with inevitable grain growth.In this work,dense and grain-refined nanocrystalline(La_(0.2)Nd_(0.2)Sm_(0.2)Gd_(0.2)Eu_(0.2))_(2)Zr_(2)O_(7)ceramics were prepared with ultra-high pressure sintering(UHPS)method under 10 GPa at a low temperature of 800℃.The densification behavior,microstructure evo-lution,and properties of the UHPS-ed samples were then investigated.The grain size of as-prepared(La_(0.2)Nd_(0.2)Sm_(0.2)Gd_(0.2)Eu_(0.2))_(2)Zr_(2)O_(7)ceramic was only 151 nm,which is 40%smaller than that of raw pow-der.In addition,it exhibited advantageous properties including both high hardness and aqueous durabil-ity.Plastic deformation under ultra-high pressure was believed as the dominant densification mechanism responsible for grain refinement and property improvement.
基金
financially supported by the National Natu-ral Science Foundation of China(nos.92163208,51902233,and 51972243)
the National Key Research and Development Plan of China(no.2021YFB3701400)
the Independent Innovation Projects of the Hubei Longzhong Laboratory(no.2022ZZ-11).