The presence of Li_(2)Si_(2)O_(5) and LiAlSi_(4)O_(10) could effectively improve the elastic modulus and transmittance of lithium disilicate(LD)glass-ceramics.Through synergistically modulation of the crystal content and grain size,we obtained high strength and high transmittance of LD glass-ceramics.The optimal sample had a high transmittance of 90.3%,the hardness was 7.72 GPa,the fracture toughness was 1.07 MPa·m^(1/2),and the elastic modulus was 103.1 GPa.
作者
胡云坤
RAO Yu
WANG Mingzhong
XU Yinsheng
XIA Mengling
TAO Haizheng
陆平
HU Yunkun;RAO Yu;WANG Mingzhong;XU Yinsheng;XIA Mengling;TAO Haizheng;LU Ping(School of Materials Science and Engineering,Wuhan University of Technology,Wuhan 430070,China;Xianning CSG Photovoltaic Glass Co.,Ltd.,Xianning 437100,China;State Key Laboratory of Silicate Materials for Architectures,Wuhan University of Technology,Wuhan 430070,China;Jincheng Optical-mechanical Industry Research Institute,Jincheng 048000,China)
基金
Funded by the National Natural Science Foundation of China(No.52372014)
the Key R&D Project of Hubei Province(No.2022BAA025)
the Key R&D Project of Jincheng City(No.20220120)。