摘要
The influence of different cryogenic sequences on the rolling contact fatigue(RCF)life of M50-bearing steel has been studied.The results show that direct cryogenic treatment after quenching can effectively improve RCF life.The L_(10)life is strikingly 5 times longer than that with cryogenic treatment after tem-pering.This is caused by the distinct lattice construction of martensite and the transformation of retained austenite.More secondary nanocarbides and fine twins are formed via cryogenic treatment before tem-pering compared with cryogenic treatment after tempering.The improvement in the RCF life of the steel is attributed to the joint effects of the secondary nanocarbides and twin boundaries with a width of 5-13 nm,which delays significantly crack initiation and propagation.This study highlights a common method to improve the service life of high-carbon and high-alloy steels by adjusting the cryogenic se-quence.
基金
supported by the National Natural Science Foun-dation(Grant No.52031013)
the National Key Research and Development Program(Grant No.2018YFA0702900).