摘要
以丙二醇甲醚为分散介质,通过棒硝式砂磨的工艺制备复合铁钛粉纳米防腐色浆。通过对砂磨后色浆的沉降试验,确定了色浆的最佳的砂磨时间为8 h。通过研究改性剂添加前后对防腐色浆沉降高度、颗粒形貌、粒径分布和zeta电位的影响,最终确定以添加了GL-1110改性剂后所制备的复合铁钛粉纳米防腐色浆最为稳定,其粒径小于10μm,具有较好的分散性。
The iron titanium powder anticorrosive paste was prepared by the process of sand milling in propylene glycol methyl ether.The optimum sanding time of the paste was 8 h,which was determined by the sedimentation test.The settling height,particle morphology,particle size distribution and zeta potential of the anticorrosive pastes were compared before and after modification.It was finally determined that the most stable anticorrosive paste system was the one modified with GL-1110.The particle size of the composite iron titanium powder nano-anticorrosive paste prepared was less than 10μm,and it had good dispersibility.
作者
林光宁
林清华
Lin Guangning;Lin Qinghua(Guangdong Power Supply Bureau Co.,Ltd.,Yangjiang Guangdong,529500,China)
出处
《上海涂料》
CAS
2024年第2期21-24,共4页
Shanghai Coatings
基金
中国南方电网项目资助:配电变压器重防腐涂层材料及在线修复技术的研究(031700KC23040010)。
关键词
防腐色浆
复合铁钛粉
纳米色浆
改性剂
anticorrosive paste
composite iron titanium powder
nano paste
modifier