以MgCl_(2)/2-乙基己醇/TiCl_(4)体系合成用于乙烯聚合的球形Ziegler-Natta催化剂,在合成催化剂过程中加入复合内给电子体:乙酸正己酯/邻酞酸二异丁酯,与分别加入四乙氧基硅烷、乙酸乙酯和邻酞酸二异丁酯内给电子体的催化剂进行对比。利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和差示扫描量热仪(DSC)等手段对含不同内给电子体的催化剂和聚合物进行分析,并通过乙烯聚合对催化剂催化性能进行评价。结果表明,在温度为80℃,压力0.5 MPa,时间2 h的条件下,含复合内给电子体乙酸正己酯/邻酞酸二异丁酯的催化剂催化乙烯聚合活性比其它单一内给电子体的催化剂催化活性要高,催化活性为1.24×10^(5)g PE/(mol_(Ti)·h)。
MgCl_(2)/2-Ethylhexanol/TiCl_(4system)was used to synthesize spherical Ziegler-Natta catalyst for ethylene polymerization,and the composite internal electron donor was added in the synthesis process:nhexyl acetate/diisobutyl phthalate was compared with tetraethoxysilane,ethyl acetate and diisobutyl phthalate as electron donors,respectively.The catalysts and polymers containing different internal electron donors were analyzed by means of X-ray diffraction(XRD),scanning electron microscopy(SEM)and differential scanning calorimetry(DSC),and the catalytic performance of the catalysts was evaluated by ethylene polymerization.The results showed that under the conditions of temperature 80℃,pressure0.5 MPa and time 2 h,the catalytic activity of the catalyst containing complex internal electron donornhexyl acetate/diisobutyl phthalate was higher than that of other single internal electron donor catalysts,and the catalytic activity was 1.24×10^(5)g PE/(mol_(Ti)·h).
作者
王俊
付兴宇
张娜
毛国梁
陈丽铎
WANG Jun;FU Xing-yu;ZHANG Na;MAO Guo-liang;CHEN Li-duo(Heilongjiang Key Laboratory of New Polyolefin Materials,College of Chemistry and Chemical Engineering,Northeast Petroleum University,Daqing 163318,China)
出处
《应用化工》
CAS
CSCD
北大核心
2024年第4期829-831,837,共4页
Applied Chemical Industry
基金
黑龙江省重点研发计划(JD22A026)
东北石油大学科研启动计划(2021KQ06)。
关键词
复合型内给电子体
聚合反应
聚乙烯
齐格勒-纳塔催化剂
compound internal electron donor
polymerization reaction
polyethylene
Ziegler-Natta catalyst