摘要
分别以麦草废渣、纤维素/半纤维素为原料,掺杂制浆废液,通过直接压缩成形,制备了生物质颗粒燃料及其模型物,并对生物质颗粒燃料的物理性能和燃烧性能进行了研究。结果表明,制浆废液中因含有木质素、糖类等有机成分而具有较好的黏结性,能够提高颗粒燃料的物理性能。由固含量4.29%的制浆废液制备的模型颗粒燃料,横向抗压强度和燃烧热值最高值分别为128.28 MPa和16 806.4 J/g,明显高于由水制备的颗粒燃料,但该模型燃料的综合燃烧特性指数降低为1.69×10^(-9)%^(2)/(min^(2)·℃^(3))。
Wheat residues and cellulose/hemicellulose as raw materials were separately mixed with pulping waste liquid to prepare biomass granular fuel and its model through direct compression molding technology.The physical performance and the combustion characteristics of granular fuel were systemically studied.The results showed that the pulping waste liquid had good adhesive property because of the presence of lignin,sugar,and other organic components,which could improve the physical properties of granular fuels.The maximum transverse compressive strength and calorific value of granular fuel prepared by pulping waste liquid with solid content of 4.29%were 128.28 MPa and 16806.4 J/g,respectively,which were obviously higher than that of the granular fuel prepared by water,whereas the comprehensive com⁃bustion characteristics index was decreased to 1.69×10^(−9)%^(2)/(min^(2)·℃^(3)).
作者
薛蓝馨
林兆云
杨桂花
陈嘉川
XUE Lanxin;LIN Zhaoyun;YANG Guihua;CHEN Jiachuan(State Key Lab of Biobased Material and Green Papermaking/Key Lab of Pulp&Paper Science and Technology of Education Ministry of China,Qilu University of Technology(Shandong Academy of Sciences),Ji’nan,Shandong Province,250353)
出处
《中国造纸》
CAS
北大核心
2024年第4期162-169,共8页
China Pulp & Paper
基金
国家重点研发计划项目(2019YFC1905904)
山东省科教产融合创新试点工程(2022JBZ01-05,2022PY57)。
关键词
制浆废液
生物质颗粒燃料
物理性能
燃烧特性
pulping waste liquid
biomass granular fuel
physical properties
combustion characteristics