摘要
采用熔化极氩弧焊对厚度为10 mm的409L热轧板进行焊接试验,将焊件平对接坡口间隙设定为1 mm、2 mm、3 mm、4 mm,其他焊接参数略有不同。焊接试验完成后对结构接头处进行背弯分析,结果表明,坡口间隙为1 mm、2 mm和3 mm的接头处出现裂纹发生断裂,而坡口间隙为4 mm的接头处组织完好,背弯试验结果合格。
The 409L hot-rolled plate with a thickness of 10 mm was welded by molten electrode argon arc welding,and the flat butt groove gap of the weldment was set to 1 mm,2 mm,3 mm,4 mm,and other welding parameters were slightly different.After the welding test was completed,the backbend analysis was carried out on the structural joints.The results showed that the joints with groove gaps of 1 mm,2 mm and 3 mm had cracks and fractures,while the joints with groove gaps of 4 mm were in good condition,and the backbending test results were qualified.
作者
邹庆华
Zou Qinghua(Shanxi Taigang Stainless Steel Co.,Ltd.,Taiyuan Shanxi 030003,China)
出处
《山西冶金》
CAS
2024年第4期63-64,共2页
Shanxi Metallurgy
关键词
铁素体不锈钢
接头间隙
背弯性能
ferritic stainless steel
joint gap
backbend performance