研究奇耐^(®)N9在全钢载重子午线轮胎胎面胶中的应用。结果表明:在胎面胶生产配方中添加2份奇耐^(®)N9,胶料的密度增大,物理性能相当,但气孔率明显下降,工艺性能改善。采用试验胶料制备的315/80R22.520PR全钢载重子午线轮胎的耐久性能和高速性能与生产轮胎没有明显差异,生产成本降低。
The application of cheenibe^(®)N9 in the tread compound of truck and bus radial tires was studied.The results showed that by adding 2 phr cheenibe^(®)N9 to the production formula of the tread compound,the density of the compound increased,the physical properties were equivalent,but the porosity decreased significantly,and the processability improved.The durability and high-speed performance of 315/80R22.520PR truck and bus radial tires prepared with the experimental compound were not significantly different from those of production tires,and the production costs were reduced.
作者
刘琦
李祥
张洪
胡录伟
杨利伟
LIU Qi;LI Xiang;ZHANG Hong;HU Luwei;YANG Liwei(Sichuan Kailiwei Technology Co.,Ltd,Jianyang 641400,China)
出处
《轮胎工业》
CAS
2024年第5期295-298,共4页
Tire Industry