Bismuth-based halide double perovskite Cs_(2)KBiCl_(6): Disorder and luminescence

A new bismuth-based halide double perovskite Cs_(2)KBiCl_(6) was isolated successfully through solid-state reactions and investigated using X-ray and neutron diffraction.Rather than an ordered structure,the crystal structure consists of shifted Cs,K,Bi,and Cl sites from the ideal positions with fractional occupancy in compensation,leading to variable local coordination of Cs^(+)ions,as revealed by^(133)Cs solid-state nuclear magnetic resonance spectroscopy.Cs_(2)KBiCl_(6) displays volume hysteresis at 5-298 K range upon heating and cooling.The Cs_(2)KBiCl_(6) has a direct bandgap of 3.35(2)eV and red-shift luminescence of around 600 nm upon Mn doping compared with the Na analogue.The stabilization of disordered structure in Cs_(2)KBiCl_(6) is related to two factors including the large-sized K^(+)cation which prefers to coordinate with more than six Cl^(-),and the Bi^(3+)with 6s^(2) lone pair which has a preference for a local asymmetric environment.These findings could have general application and help to understand the structure and property of halide perovskites.