摘要
The rapid development of information technology leads a demand for high frequency soft magnetic materials with ex-ceptional radar wave absorption properties.A new magnetic material with superior radar wave absorption is explored in this paper.we explored the preparation of Y_(2)Co_(17)-xFex(x=0.0,1.0,2.0,3.0)alloy powders using yttrium oxide as a raw material by a low-cost and short preparation cycle reduction-diffusion process.The crystal structure,intrinsic magnetic properties,high frequency magnetism and radar wave absorption of Y_(2)Co_(17)-xFex(x=0.0,1.0,2.0,3.0)were investigated.These compounds have a perfect magnetic repair of Y_(2)Co_(17) and enable the improvement of the overall magnetic properties of Y_(2)Co_(17)-xFex(x=0.0,1.0,2.0,3.0)compounds.The Y_(2)Co_(17)-xFex/Polyurethane(PU)(x=0.0,1.0,2.0,3.0)absorbers were divided in detail using the zero-reflection mechanism.The results show that all Y_(2)Co_(17)-xFex/PU(x=0.0,1.0,2.0,3.0)absorbers have excellent absorption performance(reflection loss RL is less than-85 dB);in addition,Y_(2)Co_(15)Fe_(2)/PU absorbers and Y_(2)Co_(14)Fe_(3)/PU absorbers are superior candidates for S-band materials.In particular,the perfectly matched frequency fp of the modulated Y_(2)Co_(14)Fe_(3)/PU absorber is shifted to the L-band(1–2 GHz)where early warning radars are located.The Y_(2)Co_(14)Fe_(3)/PU absorber has an effective absorption bandwidth of 300 MHz(1.5–1.8 GHz)at a thickness of 5.230 mm.It can also absorb the full L-band at-4 dB,which has rarely been reported.
基金
supported by the National Key Research and Development Program of China(Grant No.2021YFB3501302)
the National Natural Science Foundation of China(Grant No.51731001)
the Fund from the State Key Laboratory of Baiyunobo Rare Earth Resource Researches and Comprehensive Utilization’s Key Research and Development Projects.