摘要
某航天产品在装配、存储环节中,其表面耐高温涂层出现破损等现象。本文针对此问题,对其失效形式进行了模式分析与机理分析,通过试验验证了分析的正确性,并提出了该航天高温涂层材料在使用过程中的注意事项及防护措施。
In the assembly and storage of an aerospace product,the high-temperature resistant coating on the surface of the product is damaged.Aiming at this problem,the failure mode and mechanism are analyzed,and the correctness of the analysis is verified through experiments.Finally,the precautions and protective measures for the aerospace high-temperature coating in the use process are proposed.