Homogenous coating of Li^(+)conductive Li_(5)AlO_(4)on single-crystalline nonstoichiometric Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)for rechargeable lithium-ion batteries

Cobalt-free,nickel-rich LiNi_(1-x)Al_(x)O_(2)(x≤0.1)is an attractive cathode material because of high energy density and low cost but suffers from severe structural degradation and poor rate performance.In this study,we propose a molten salt-assisted synthesis in combination with a Li-refeeding induced aluminum segregation strategy to prepare Li_(5)AlO_(4)-coated single-crystalline slightly Li-rich Li_(1.04)Ni_(0.92)Al_(0.04)O_(2).The symbiotic formation of Li_(5)AlO_(4)from reaction between molten lithium hydroxide and doped aluminum in the bulk ensures a high lattice matching between the Ni-rich oxide and the homogenous conductive Li_(5)AlO_(4)that permits high Li^(+)conductivity.Benefiting from mitigated undesirable side reactions and phase evolution,the Li_(5)AlO_(4)-coated single-crystalline Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)delivers a high specific capacity of220.2 mA h g^(-1)at 0.1 C and considerable rate capability(182.5 mA h g^(-1)at 10 C).Besides,superior capacity retention of 90.8%is obtained at 1/3 C after 100 cycles in a 498.1 mA h pouch full cell.Furthermore,the particulate morphology of Li_(1.04)Ni_(0.92)Al_(0.04)O_(2)remains intact after cycling at a cutoff voltage of 4.3 V,whereas slightly Li-deficient Li_(0.98)Ni_(0.97)Al_(0.05)O_(2)features intragranular cracks and irreversible lattice distortion.The results highlight the value of molten salt-assisted synthesis and Li-refeeding induced elemental segregation strategy to upgrade Ni-based layered oxide cathode materials for advanced Li-ion batteries.