Surface-derived phosphate layer on NiFe-layered double hydroxide realizes stable seawater oxidation at the current density of 1 A·cm^(−2)

Seawater electrolysis,especially in coastlines,is widely considered as a sustainable way of making clean and high-purity H2 from renewable energy;however,the practical viability is challenged severely by the limited anode durability resulting from side reactions of chlorine species.Herein,we report an effective Cl^(−) blocking barrier of NiFe-layer double hydroxide(NiFe-LDH)to harmful chlorine chemistry during alkaline seawater oxidation(ASO),a pre-formed surface-derived NiFe-phosphate(Pi)outerlayer.Specifically,the PO_(4)^(3−)-enriched outer-layer is capable of physically and electrostatically inhibiting Cl−adsorption,which protects active Ni^(3+)sites during ASO.The NiFe-LDH with the NiFe-Pi outer-layer(NiFe-LDH@NiFe-Pi)exhibits higher current densities(j)and lower overpotentials to afford 1 A·cm^(−2)(η1000 of 370 mV versusη1000 of 420 mV)than the NiFe-LDH in 1 M KOH+seawater.Notably,the NiFe-LDH@NiFe-Pi also demonstrates longer-term electrochemical durability than NiFe-LDH,attaining 100-h duration at the j of 1 A·cm^(−2).Additionally,the importance of surface-derived PO_(4)^(3−)-enriched outer-layer in protecting the active centers,γ-NiOOH,is explained by ex situ characterizations and in situ electrochemical spectroscopic studies.