摘要
采用透射电镜(TEM)、高分辨率透射电镜(HRTEM)和能谱仪(EDS)对铸造Be-Al合金的界面进行研究。结果表明,Be-Al界面上没有发生界面反应,界面结合良好。铸态Be-Al合金的界面几何结构为半共格界面,Be-Al界面为Be(0001)/Al(110)基面相结合,同时,界面处存在BeO和Al_(2)O_(3)颗粒。
The interface of cast beryllium aluminum alloy was investigated by transmission electron microscopy(TEM),high-resolution transmission electron microscopy(HRTEM)and energy dispersive spectrometry(EDS).The results indicate that absence of interfacial reaction is observed at the Be-Al interface with satisfied bonding.The interface geometry of as-cast Be-Al alloy is a semi-coherent interface,and the Be-Al interface is a combination of Be(0001)/Al(110)base planes.Meanwhile,BeO and Al_(2)O_(3) particles exist at the interface.
作者
杨一群
王东新
张鹏
李军义
谢垚
刘兆刚
李正飞
吴梓裴
YANG Yiqun;WANG Dongxin;ZHANG Peng;LI Junyi;XIE Yao;LIU Zhaogang;LI Zhengfei;WU Zipei(State Key Laboratory of Rare Metal Special Materials,Northwest Institute of Rare Metal Materials,Shizuishan 753000)
出处
《特种铸造及有色合金》
CAS
北大核心
2024年第7期946-948,共3页
Special Casting & Nonferrous Alloys
基金
国家重点研发计划资助项目(2021YFC2902304)
宁夏回族自治区重点研发计划资助项目(2023BDE02010,2022BDE92022)
国家自然科学联合基金资助项目(U23A20612)
高端金属材料创新联合体资助项目(LHT-2023-014)
宁夏自然科学基金资助项目(2023AAC03894,2023AAC03893)
稀有金属特种材料国家重点实验室开放课题基金资助项目(SKL2023K00X)。
关键词
铸造铍铝合金
界面
HRTEM
精密铸造
As-cast Beryllium Aluminum Alloy
Interface
HRTEM
Investment Casting