Impact of Mo/Ni alloying on microstructural modulation and low-temperature toughness of high-strength low-alloy steel

The high-strength low-alloy steel plates with varying Ni/Mo contents were manufactured using the thermos-mechanical control process.The investigation was conducted to explore the effect of Ni/Mo microalloying on microstructure evolution and mechanical properties of the steel.The results revealed that the increase in Ni content from 1 to 2 wt.%reduced the transition temperature of ferrite and the growth range of ferritic grain was narrowed,which promoted grain refinement.The optimized combination of grain size,high-angle grain boundaries(HAGBs),and martensite-austenite(M-A)islands parameter contributed to the excellent impact toughness of S1 steel at-100℃(impact absorbed energy of 218.2 J at-100℃).As the Mo increases from 0 to 2 wt.%,the matrix structure changes from multiphase structure to granular bainite,which increases the average effective grain size to~4.62 pm and reduces HAGBs proportion to~36.22%.With these changes,the low-temperature impact toughness of S3 steel is weakened.In addition,based on the analysis of the characteristics of crack propagation path,it was found that M-A islands with low content(~2.21%)and small size(~1.76 pm)significantly retarded crack propagation,and the fracture model of M-A islands with different morphologies was further proposed.Furthermore,correlation between behaviour of delamination and toughness was further analysed by observing delamination size and impact energy parameters.