Achieving high strength and rapid degradation in Mg-Gd-Ni alloys by regulating LPSO phase morphology combined with extrusion

In this study,Mg-13.2Gd-4.3Ni alloys containing continuous bulk-shaped long-period stacking ordered(LPSO),lamellar LPSO,and a small amount of eutectic phase were prepared,and the evolution of microstructure at different extrusion temperatures and its influence on mechanical and degradation properties as well as corrosion mechanism were investigated.Preheating before extrusion can effectively promote the precipitation of lamellar LPSO in matrix.EX400 with higher volume fraction of non-DRXed grains exhibited higher strength,which was mainly due to strong texture,high dislocation density,and high volume fraction of lamellar LPSO.The EX420 with higher volume fraction of DRXed grains showed higher degradation rate,which was mainly due to the higher density of grain boundary.The EX400 exhibited excellent comprehensive properties with tensile yield strength(TYS)of 334 MPa,ultimate tensile strength(UTS)of 484 MPa and elongation(EL)of 7.4%,ultimate compressive strength(UCS)of 638 MPa and compressive yield strength(CYS)of 443 MPa,degradation rate of 86.1 mg/cm^(2)/h at 93℃in 3 wt.%KCl solution.