The wetting behavior of molten Cu on the B_(4)C-xTiB_(2)ceramic composites was investigated in this work.The results show that the contact angle of molten Cu alloy on B_(4)C-TiB_(2)ceramic composites is linear with the composition rate of TiB_(2)or B_(4)C while the temperature is in the range of 1300 to 1350℃,consistent with the expectation of the commonly used theoretical method.However,a nonlinear relationship between the contact angle and the composition rate unexpectedly occurred at temperatures ranging from 1400 to 1500℃.The big difference of the contact angles between the molten metal and the components in the composites was found to be the key point.This result identifies that the commonly used theoretical method only works at a limited difference of the contact angle of the liquid on the different phases in the composites,and fails at a big difference.