利用己内酯与木质素反应制备了改性木质素,将改性木质素、交联剂、硫磺与间规聚丙烯(s PP)共混,通过双螺杆挤出制备了微交联抗冲s PP复合材料。测试了微交联抗冲s PP复合材料的力学性能、流动性和热稳定性等。实验结果表明:当间规聚丙烯、交联剂、改性木质素、硫磺添加份数比例为100/0.2/1.0/0.3时,复合材料的力学性能较好,弯曲最大强度和冲击强度相对纯间规聚丙烯分别提高了11%和116%。
An modification agent was prepared through the reaction of caprolactone and lignin.This agent,along with a crosslinking agent and sulfur,was blended with syndiotactic polypropylene(sPP),resulting in a micro-crosslinked sPP composite prepared through extrusion crosslinking.The mechanical properties,fluidity and thermal stability of the resulting micro-crosslinked sPP composites were tested.Experimental results indicated that the composite achieved optimal mechanical properties with a ratio of PP,crosslinking agent,modification agent,and sulfur at 100/0.2/1.0/0.3,and the maximum bending strength and impact strength of the composite were increased by 11%and 116%,respectively,compared with pure sPP.
作者
夏先荣
龙华月
程睿智
苏胜培
张燕
XIA Xian-rong;LONG Hua-yue;CHENG Rui-zhi;SU Sheng-pei;ZHANG Yan(College of Chemistry and Chemical Engineering,Hunan Normal University,Changsha 410081,China;National&Local Joint Engineering Laboratory for New Petro-chemical Materials and Fine Utilization of Resources,Changsha 410081,China)
出处
《精细化工中间体》
CAS
2024年第4期57-63,77,共8页
Fine Chemical Intermediates
关键词
微交联
抗冲击
聚丙烯复合材料
microcrosslinking
impact resistance
polypropylene composite