Vacuum-free lamination via controlled polymer adhesion for selective photogeneration and photodetection

This study attempts to develop a reproducible thin-film formation technique called vacuum-free(VF)lamination,which transfers thin films using elastomeric polymer-based laminating mediators.Precisely,by controlling the interface characteristics of the mediator based on the work of adhesion,VF lamination is successfully performed for various thicknesses(from 20 to 240 nm)of a conjugated photoactive material composed of poly[(2,6-(4,8-bis(5-(2-ethylhexyl-3-fluoro)thiophen-2-yl)-benzo[1,2-b:4,5-bʹ]dithiophene))-alt-(5,5-(1ʹ,3ʹ-di-2-thienyl-5ʹ,7ʹ-bis(2-ethylhexyl)benzo[1ʹ,2ʹ-c:4ʹ,5ʹ-cʹ]dithiophene-4,8-dione)](a polymer donor)and 2,2ʹ-((2Z,2ʹZ)-((12,13-bis(2-butyloctyl)-3,9-diundecyl-12,13-dihydro-[1,2,5]thiadiazolo[3,4-e]thieno[2ʹʹ,3ʹʹ:4ʹ,5ʹ]thieno[2ʹ,3ʹ:4,5]pyrrolo[3,2-g]thieno[2ʹ,3ʹ:4,5]thieno[3,2-b]indole-2,10-diyl)bis(methanylylidene))bis(5,6-difluoro-3-oxo-2,3-dihydro-1H-indene-2,1-diylidene))dimalononitrile(a nonfullerene acceptor).Interestingly,the organic photovoltaic and photodetecting applications,prepared by the VF lamination process,showed superior performance compared to those of devices prepared by conventional spin-coating.This is due to the overturned surface morphology,which led to enhanced charge transport ability and blocking of the externally injected charge.Thus,the reproducible VF lamination process,exploiting an adhesion-based elastomeric polymer mediator,is a promising thin-film formation technique for developing efficient next-generation organic optoelectronic materials consistent with the solution process.