Highly Strong,Tough,and Cryogenically Adaptive Hydrogel Ionic Conductors via Coordination Interactions

Despite the promise of high flexibility and conformability of hydrogel ionic conductors,existing polymeric conductive hydrogels have long suffered from compromises in mechanical,electrical,and cryoadaptive properties due to monotonous functional improvement strategies,leading to lingering challenges.Here,we propose an all-in-one strategy for the preparation of poly(acrylic acid)/cellulose(PAA/Cel)hydrogel ionic conductors in a facile yet effective manner combining acrylic acid and salt-dissolved cellulose,in which abundant zinc ions simultaneously form strong coordination interactions with the two polymers,while free solute salts contribute to ionic conductivity and bind water molecules to prevent freezing.Therefore,the developed PAA/Cel hydrogel simultaneously achieved excellent mechanical,conductive,and cryogenically adaptive properties,with performances of 42.5 MPa for compressive strength,1.6 MPa for tensile strength,896.9%for stretchability,9.2 MJ m^(−3)for toughness,59.5 kJ m^(−2)for fracture energy,and 13.9 and 6.2 mS cm^(−1)for ionic conductivity at 25 and−70°C,respectively.Enabled by these features,the resultant hydrogel ionic conductor is further demonstrated to be assembled as a self-powered electronic skin(e-skin)with high signal-to-noise ratio for use in monitoring movement and physiological signals regardless of cold temperatures,with hinting that could go beyond high-performance hydrogel ionic conductors.