Catalytic Performance of Aquathermolysis and Viscosity Reduction of Heavy Oil over a WO_(3)/ZrO_(2) Solid Acid

Tungstated zirconia(WO_(3)/ZrO_(2))solid acid catalysts with different WO_(3) contents were prepared by a hydrothermal method and then used in the catalytic aquathermolysis of heavy oil from Xinjiang.The WO_(3)/ZrO_(2) solid acid catalyst was characterized by a range of characterization methods,including X-ray diffraction,NH3-temperature programmed desorption,and pyridine infrared spectroscopy.The WO_(3) content of the WO_(3)/ZrO_(2) catalysts had an important impact on the structure and property of the catalysts.When the WO_(3) mass fraction was 20%,it facilitated the formation of tetragonal zirconia,thereby enhancing the creation of robust acidic sites.Acidity is considered to have a strong impact on the catalytic performance of the aquathermolysis of heavy oil.When the catalyst containing 20%WO_(3) was used to catalyze the aquathermolysis of heavy oil under conditions of 14.5 MPa,340℃,and 24 h,the viscosity of heavy oil decreased from 47266 to 5398 mPa·s and the viscosity reduction rate reached 88.6%.The physicochemical properties of heavy oil before and after the aquathermolysis were analyzed using a saturates,aromatics,resins,and asphaltenes analysis,gas chromatography,elemental analysis,densimeter etc.After the aquathermolysis,the saturate and aromatic contents significantly increased from 43.3%to 48.35%and 19.47%to 21.88%,respectively,with large reductions in the content of resin and asphaltene from 28.22%to 25.06%and 5.36%to 2.03%,respectively.The sulfur and nitrogen contents,and the density of the oil were significantly decreased.These factors were likely the main reasons for promoting the viscosity reduction of heavy oil during the aquathermolysis over the WO_(3)/ZrO_(2) solid acid catalysts.