The electrochemical performance of 317L stainless steel used in medicineunder different conditions of passivation (different contents of HNO_3 solution, differentpassivation time and different passivation temperatures) was studied. The results show that thepitting potential of 317L stainless steel used in medicine can reach about 1.0 V (SCE) whenelectrochemically tested in 0.9% NaCl solution after the steel was passivated in 30% HNO_3 solutionat 35℃ for 6 h, which indicates that the passivation film has a relatively strong resistance tocorrosion. The results also show that the corrosion resistance of the passivation film on thesurface of 317SS can be increased after suitable amount of K_2Cr_2O_7 is added into HNO_3passivation solution.
The electrochemical performance of 317L stainless steel used in medicineunder different conditions of passivation (different contents of HNO_3 solution, differentpassivation time and different passivation temperatures) was studied. The results show that thepitting potential of 317L stainless steel used in medicine can reach about 1.0 V (SCE) whenelectrochemically tested in 0.9% NaCl solution after the steel was passivated in 30% HNO_3 solutionat 35℃ for 6 h, which indicates that the passivation film has a relatively strong resistance tocorrosion. The results also show that the corrosion resistance of the passivation film on thesurface of 317SS can be increased after suitable amount of K_2Cr_2O_7 is added into HNO_3passivation solution.