摘要
采用粉末冶金方法制备了新型La2O3-Gd2O3-Mo次级发射材料.测试了其次级发射性能.实验结果表明,在钼中加入稀土氧化物可以具有很好的次级发射性能,其次级发射性能与激活温度密切相关.经过1360℃的激活处理后,该材料的最大次级发射系数可达2.65,超过了材料使用要求的2.0的发射水平.
The powder metallurgy method was adopted to prepare the new type secondary emission material. The result of testing its emission performance shows that the molybdenum added with rare earth oxides may have good secondary emission performance, which has much to do with the activation temperature. After activating treatment at 1 360 ℃, the maximum secondary emission coefficient of this material may reach 2.65, exceding the application demand of the material(2.0).