摘要
The effect of resin structure on desalination of lignin solution was investigated,the optimal structure of resin is as follows;cross linking degree as 4%,ratio of cationogen to anionogen is near 1.with such resin the desalination of lignin was produced very well because the resin has both molecule sieving and ion retardation properties.The sulfonation degress of lignin and total salt content of lignin solution were determinred with ion exchange technique,the relative error less than 1%.The salt content of small molecule in the lignin solution was calculated from sulfonation degree of lignin and total salt.Among gel and macroporous resins the best separation of lignin from reducing sugar was achieved with interpenetrating sulfonated resin 2×1.5×1.The separation of lignin with interpenetrating resin was carried out simultaneously with fractionation of lignin,the effect of fractionation with macroporous sulfonated resin is better than that with interpenetrating resin,but the former has a definite sorption of lignin which decreased the recovery of lignin.
The effect of resin structure on desalination of lignin solution was investigated, the optimal structure of resin is as follows; cross linking degree is 4% , ratio of cationogen to anionogen is near 1. with such resin the desalination of lignin was produced very well because the resin has both molecule sieving and ion retardation properties. The sulfonation degree of lignin and total salt content of lignin solution were determinred with ion exchange technique, the relative error less than 1 %. The salt content of small molecule in the lignin solution was calculated from sulfonation degree of lignin and total salt. Among gel and macroporous resins the best separation of lignin from reducing sugar was achieved with interpenetrating sulfonated resin 2×1. 5×1. The separation of lignin with interpenetrating resin was carried out simultaneously with fractionation of lignin, the effect of fractionation with macroporous sulfonated resin is better than that with interpenetrating resin, but the former has a definite sorption of lignin which decreased the recovery of lignin.