摘要
In this article,AHPS(3-allyloxy-2-hydroxy-1-propanesulfonate salt) was synthesized to use in emulsifier-free emulsion polymerization of BA/BMA/MMA system for high solid content latexes.Storage stability,flow behavior of the latexes,morphology of the obtained latex particles,dynamic viscoelastic behavior,tensile strength and water resistance properties of the resulted copolymers were investigated.The experimental results show that with the addition of AHPS,stability of the emulsion is greatly improved that there appears no apparent precipitation during the polymerization and storage at room temperature for 6 months and at -10℃ for four months.Flow of the latexes follows the Bingham body laws,diameter of the latex particles is about 0.6μm,of which is larger than that of by conventional emulsion polymerization(0.12μm).In addition,not only water resistance of the copolymers obtained by emulsifier-free emulstion polymerization is greatly improved,but also tensile strength is obviously enhanced.
In this article, AHPS (3 - allyloxy- 2 -hydrory- 1 -Propanesulfonate salt) wassynthesized to use in emulsifier-Ne emulsion polymerization of BA/BMa/MMA systemfor high solid content latexes. Storage stability klow behavior of the latexes,morphology of the obtained latex particles, dynamic viscoelastic behavior, tensilestrength and water resistance properties of the resulted copolymers were investigated.The experimental results show that with the addition of AHPS, stability of the emulsionis greatly improved that there appears no apparent precipitation dunring thepolymerization and storage at room temperature for 6 months and at -10℃ for fourmonths. Flow of the latexes follows the Bingham body laws, diameter of the latexparticles is about 0.6μn, of which is larger than that of by conventional emulsionpolymerization(0.12μm). In addition, not only water resistance of the copolymersobtained by emulsifier-free emulsion polymerization is greatly improved, but alsotensile strength is obviously enhanced.