摘要
The pH dependence of the extrapolated shear yield stress for Alcoa A16 α-Al2O3 suspensions at the powder volume fraction of 0.27 with and without addition of both polyvinyl alcohol (PVA) and polyethylene glycol (PEG) each at fixed 0.18% of the powder mass was studied. Whith the polymer added, the full deflocculation of the suspension shifts from about pH=4 to around pH=1.5, at which the minimum value of shear yied stress is higher than that at pH=4. The addition of both PVA and PEG was found to prevent the filter cake from cracking.
The pH dependence of the extrapolated shear yield stress for Alcoa A16 a-Al2O3 suspensions at the powder volume fraction of 0.27 with and without addition of both polyvinyl alcohol (PVA) and polyethylene glycol (PEG) each at fixed 0.18% of the powder mass was studied. With the polymer added, the full deflocculation of the suspension shifts from about pH=4 to around pH=1.5, at which the minimum value of shear yield stress is higher than that at pH=4. The addition of both PVA and PEG was found to prevent the filter cake from cracking.