Mg0-Al2O3-Cr2O3 ramming mixes made of different raw materials have different mineral structure and different physical properties though with the identical particle size distribution, the same amount of binder and chemical composition . The residual carbon content of the fused magnesia-chrome material made in reducing atmosphere is very high, if this material is used in the MgO-Al203-Cr2O3 ramming mix , it would cause spalling of the furnace lining during drying-out.
Mg0-Al2O3-Cr2O3 ramming mixes made of different raw materials have different mineral structure and different physical properties though with the identical particle size distribution, the same amount of binder and chemical composition . The residual carbon content of the fused magnesia-chrome material made in reducing atmosphere is very high, if this material is used in the MgO-Al203-Cr2O3 ramming mix , it would cause spalling of the furnace lining during drying-out.