摘要
Hexavalent chromium, Cr(VI), a highly toxic oxyanion known as a carcinogen and mutagen,is an issue of concern due to its adverse impact on human health. Therefore, development of effective technologies and/or materials for Cr(VI) removal from water has been of great interest for researchers. In this study, an electrospun carbon nanofiber(CNF) mat was prepared via electrospinning polyacrylonitrile(PAN), followed by thermal pre-oxidation and carbonization. Scanning electron microscopy(SEM) observation showed that the fiber diameter of the CNF with carbonization temperature of 950°C(CNF_(950)) was about 266 nm.Potentiometric titration analysis demonstrated that the point of zero charge p H(pHpzc) of CNF_(950) was around 7.93. CNF_(950) demonstrated high adsorption capacity and fast adsorption kinetics for Cr(VI) at pH < 3. Langmuir isotherm calculations showed that the maximum adsorption capacity of Cr(VI) on CNF_(950) was 118.8 mg/g at pH 2. The adsorption isotherm of Cr(VI) on CNF_(950) was well described by the Redlich–Peterson model, revealing that Cr(VI)adsorption was the result of a combination of monolayer and multilayer adsorption,depending on the initial Cr(VI) concentration. Solution pH greatly affected Cr(VI) adsorption onto CNF_(950) due to the electrostatic interaction, and the adsorption capacity was relatively high when pH was below 3. X-ray photoelectron spectroscopy(XPS) analysis revealed that the removal of Cr(VI) might be the result of a combination of redox reaction and electrostatic adsorption. The adsorption-saturated CNF_(950) could be regenerated by NaOH solution. This study extends the potential applicability of electrospun CNF mats for Cr(VI)-contaminated water purification.
Hexavalent chromium, Cr(VI), a highly toxic oxyanion known as a carcinogen and mutagen,is an issue of concern due to its adverse impact on human health. Therefore, development of effective technologies and/or materials for Cr(VI) removal from water has been of great interest for researchers. In this study, an electrospun carbon nanofiber(CNF) mat was prepared via electrospinning polyacrylonitrile(PAN), followed by thermal pre-oxidation and carbonization. Scanning electron microscopy(SEM) observation showed that the fiber diameter of the CNF with carbonization temperature of 950°C(CNF_(950)) was about 266 nm.Potentiometric titration analysis demonstrated that the point of zero charge p H(pHpzc) of CNF_(950) was around 7.93. CNF_(950) demonstrated high adsorption capacity and fast adsorption kinetics for Cr(VI) at pH < 3. Langmuir isotherm calculations showed that the maximum adsorption capacity of Cr(VI) on CNF_(950) was 118.8 mg/g at pH 2. The adsorption isotherm of Cr(VI) on CNF_(950) was well described by the Redlich–Peterson model, revealing that Cr(VI)adsorption was the result of a combination of monolayer and multilayer adsorption,depending on the initial Cr(VI) concentration. Solution pH greatly affected Cr(VI) adsorption onto CNF_(950) due to the electrostatic interaction, and the adsorption capacity was relatively high when pH was below 3. X-ray photoelectron spectroscopy(XPS) analysis revealed that the removal of Cr(VI) might be the result of a combination of redox reaction and electrostatic adsorption. The adsorption-saturated CNF_(950) could be regenerated by NaOH solution. This study extends the potential applicability of electrospun CNF mats for Cr(VI)-contaminated water purification.
基金
financial support received from the National Natural Science Foundation of China(Nos.51578525,5153000136 and 21407142)
Science and Technology Planning Project of Fujian Province(No.2016H0042)
Science and Technology Planning Project of Xiamen City(No.2017S0065)
the Hundred Talents Program of the Chinese Academy of Sciences