借鉴国标胶粘剂拉伸剪切强度测定方法测定了阳极、阴极环氧电泳漆与环氧涂料在底材为铝合金及钢材上漆膜的拉伸剪切强度。在铝件及钢铁件表面上阳极电泳漆漆膜的拉伸剪切强度为11.60MPa及17.91MPa;阴极电泳漆漆膜分别为17.60MPa及23.20MPa;喷涂环氧漆膜为7.93MPa及13.40MPa。并介绍了测定试验中的实际操作经验和技术细节。
The tensile shearing strength of anodic and cathodic epoxy electrophoretic coatings and spray epoxy painting on aluminium alloy and steel were determined according to national standard of tensile shearing strength determination method for adhesives. On aluminium and steel surfaces, the tensile shearing strength of anodic epoxy electrophoretic film are 11.60 MPa and 17.91 MPa respectively. For cathodic epoxy electrophoretic film are 17.60 MPa and 23.20 MPa respectively. For spray epoxy painting are 7.93 MPa and 13.40 MPa respectively. The operating experiences and technical details in this testing are described.