摘要
The synthesis of oilsoluble boron phenolic resins was studied.Thermogravimetric analysis(TG) showed that the initial decomposition temperature was about 360℃ and its heatresistance was better than that of ordinary phenolic resins.The IR peak at 1750cm-1 shows that long branch chains of organic molecules of tung oil have been bonded on the skeleton of boron phenolic resins,thus increasing its oil solubility.
The synthesis of oilsoluble boron phenolic resins was studied.Thermogravimetric analysis(TG) showed that the initial decomposition temperature was about 360℃ and its heatresistance was better than that of ordinary phenolic resins.The IR peak at 1750cm-1 shows that long branch chains of organic molecules of tung oil have been bonded on the skeleton of boron phenolic resins,thus increasing its oil solubility.