A new method (liquidus casting) was used for 356 Al alloy semi-solid slurry making. The structures of 356 Al alloy cast by a Fe mould and semi-continuous casting machine at different temperatures were investigated. How the globular grains form was also discussed. The results show that either being cast by single Fe mould or semi-continuous machine, the micro structures are not conventional dendrites but fine and net-globular grains. The average gram size is smaller than 30μm and suitable enough for thixoforming, meanwhile it can improve the mechanical properties of following products. Under the suitable casting velocity and cooling intensity, most of global grains prolong their global growth and collide with each other before dendritic growth because of the large amount of the nucleation sites.
A new method (liquidus casting) was used for 356 Al alloy semi-solid slurry making. The structures of 356 Al alloy cast by a Fe mould and semi-continuous casting machine at different temperatures were investigated. How the globular grains form was also discussed. The results show that either being cast by single Fe mould or semi-continuous machine, the micro structures are not conventional dendrites but fine and net-globular grains. The average gram size is smaller than 30μm and suitable enough for thixoforming, meanwhile it can improve the mechanical properties of following products. Under the suitable casting velocity and cooling intensity, most of global grains prolong their global growth and collide with each other before dendritic growth because of the large amount of the nucleation sites.
基金
This work was supported by The National Natural Science Foundation of China (Grant No. 59974009).