Re-recognition of the Effects of Phosphorus and Boron on the γ’’ and γ’ Phases in IN718 Alloy

Re-recognition of the Effects of Phosphorus and Boron on the γ’’ and γ’ Phases in IN718 Alloy
原文传递
导出
摘要 The effects of P and B on the matrix strength and precipitations of γ’ and γ’’ phases in the grain interior were re-recognized in this study. The combination addition of P and B markedly accelerated the precipitations of γ’ and γ’’ phases and strengthened the matrix of IN718 alloy when air-cooled from high temperature, while made no difference when waterquenched from high temperature. The effect of single addition of P on the precipitations of γ’’ and γ’ phases was the same with that of the combination addition of P and B, while the single addition of B had no effect on the precipitations of the two phases. Therefore, it was P rather than B which accelerated the precipitations of γ’ and γ’’ phases. P could take part in the precipitations of γ’ and γ’’ phases, which was revealed by electrochemical extraction and quantitative analysis of chemical composition. It also revealed that P atoms were dissolved in the c matrix to a relatively high degree at the temperature that γ’ and γ’’ phases began to precipitate, and consequently the precipitations of γ’ and γ’’ phases were accelerated. The first-principle calculation indicated that P decreased the formation enthalpies of γ’ and γ’’ phases when it occupied the Ni lattice sites in the two phases, which explained the effect of P on the γ’ and γ’’ phases. The effects of P and B on the matrix strength and precipitations of γ’ and γ’’ phases in the grain interior were re-recognized in this study. The combination addition of P and B markedly accelerated the precipitations of γ’ and γ’’ phases and strengthened the matrix of IN718 alloy when air-cooled from high temperature, while made no difference when waterquenched from high temperature. The effect of single addition of P on the precipitations of γ’’ and γ’ phases was the same with that of the combination addition of P and B, while the single addition of B had no effect on the precipitations of the two phases. Therefore, it was P rather than B which accelerated the precipitations of γ’ and γ’’ phases. P could take part in the precipitations of γ’ and γ’’ phases, which was revealed by electrochemical extraction and quantitative analysis of chemical composition. It also revealed that P atoms were dissolved in the c matrix to a relatively high degree at the temperature that γ’ and γ’’ phases began to precipitate, and consequently the precipitations of γ’ and γ’’ phases were accelerated. The first-principle calculation indicated that P decreased the formation enthalpies of γ’ and γ’’ phases when it occupied the Ni lattice sites in the two phases, which explained the effect of P on the γ’ and γ’’ phases.
出处 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2019年第3期372-380,共9页 金属学报(英文版)
关键词 IN718 SUPERALLOY PHOSPHORUS and BORON γ’’ and γ’phases HARDNESS IN718 superalloy Phosphorus and boron γ’’ and γ’phases Hardness
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部