The electrochemical formation processes of holmium-cobalt alloys on cobaltcathode in molten HoCl_3-KCl were investigated by cyclic voltammetry and open current potential-timecurve alter potentiostatic electrolysis. The structure of Ho-Co alloys' films deposited on cobaltelectrode by potentiostatic electrolysis was characterized by X-ray diffraction. The standard Gibbsfree energies of formation for the intermetallic compounds of Ho and Co were determined. Thediffusion coefficient and diffusion activation energy of Ho atom in the alloy phase were calculatedto be 10^(-10) -10^(-11) cm^2/s and 96.0 kJ/mol, respectively, from the current-time curve atpotential step.
The electrochemical formation processes of holmium-cobalt alloys on cobaltcathode in molten HoCl_3-KCl were investigated by cyclic voltammetry and open current potential-timecurve alter potentiostatic electrolysis. The structure of Ho-Co alloys' films deposited on cobaltelectrode by potentiostatic electrolysis was characterized by X-ray diffraction. The standard Gibbsfree energies of formation for the intermetallic compounds of Ho and Co were determined. Thediffusion coefficient and diffusion activation energy of Ho atom in the alloy phase were calculatedto be 10^(-10) -10^(-11) cm^2/s and 96.0 kJ/mol, respectively, from the current-time curve atpotential step.