A novel inorganic organic hybrid material, Fe 2O(OH)(C 5H 4 ~NCOO)SO 4 was synthesized via solvothermal route using a reaction of FeCl 3·6H 2O, KCNS, and 4 cyanopyridine in aqueous solution of H 2O 2 and ethanol at 130 ℃ for 3 d. The compound crystallized in monoclinic space group P 2 1, with cell parameters a =0 73850(15) nm, b =0 65100(13) nm, c =1 0546(2) nm, β =90 36(3)°, V =0 50700(18) nm 3 and Z =2. The structure is constructed with inorganic layered [Fe 2O(OH)SO 4] + cations linked by organic (C 5H 4NCOO) - anions. The compound is thermally stable up to approximately 240 ℃.
A novel inorganic organic hybrid material, Fe 2O(OH)(C 5H 4 ~NCOO)SO 4 was synthesized via solvothermal route using a reaction of FeCl 3·6H 2O, KCNS, and 4 cyanopyridine in aqueous solution of H 2O 2 and ethanol at 130 ℃ for 3 d. The compound crystallized in monoclinic space group P 2 1, with cell parameters a =0 73850(15) nm, b =0 65100(13) nm, c =1 0546(2) nm, β =90 36(3)°, V =0 50700(18) nm 3 and Z =2. The structure is constructed with inorganic layered [Fe 2O(OH)SO 4] + cations linked by organic (C 5H 4NCOO) - anions. The compound is thermally stable up to approximately 240 ℃.