60Si2MnA钢片弹簧断裂失效分析 被引量:6

Failure Analysis on Fracture of 60Si2MnA Steel Leaf Springs
下载PDF
导出
摘要 某60Si2MnA钢片弹簧在使用10h后出现批量断裂,对断裂片弹簧进行了化学成分分析、硬度测试、金相检验以及断口微观形貌观察,以查明其断裂原因。结果表明:片弹簧断裂是由于在酸洗、电镀过程中析氢反应的发生,使其产生氢脆现象;同时由于热处理工艺过程控制不当,造成组织异常,硬度高于技术要求,加快了其氢脆倾向,最终导致片弹簧在外应力作用下发生氢脆断裂。 Mass fracture appearance happened to 60Si2 MnA steel leaf springs after service only for 10 h,and means such as chemical compositions analysis,hardness testing,metallographic examination and micro fracture analysis were used to find out the fracture reasons.The results show that the hydrogen evolution reaction happening in the process of pickling and electroplating made the leaf springs produce hydrogen embrittlement phenomenon.At the same time,the improper heat treatment operations resulted in abnormal microstructure and higher hardness than the technical requirement,which accelerated the hydrogen embrittlement tendency of the leaf springs and eventually led to hydrogen embrittlement fracture under the action of external stress.
出处 《理化检验(物理分册)》 CAS 2015年第2期129-131,共3页 Physical Testing and Chemical Analysis(Part A:Physical Testing)
关键词 片弹簧 断裂 氢脆 析氢反应 热处理工艺 leaf spring fracture hydrogen embrittlement hydrogen evolution reaction heat treatment process
  • 相关文献

参考文献7

二级参考文献6

  • 1陶春虎 等.航空装备失效典型案例分析[M].北京:国防工业出版社,1998..
  • 2陶春虎 钟培道 王仁智 等.航空发动机转动部件的失效与预防[M].北京:国防工业出版社,2000.337.
  • 3陶春虎编.航空装备失效典型案例分析[M].北京:国防工业出版社, 1998.
  • 4航空航天工业部失效分析中心.航空机械失效案例选编[M].北京:科学出版社,1988.
  • 5航空航天工业部失效分析中心.金属材料断口分析及图谱[M].北京:科学出版社,1991.
  • 6余志刚.20SiMn2MoVA钢氢脆断口的分析及消除[J].理化检验(物理分册),2003,39(7):338-340. 被引量:7

共引文献56

同被引文献38

引证文献6

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部