对比研究三相合金镀层钢丝帘线与无钴胶料的粘合性能以及黄铜镀层钢丝帘线与含钴胶料的粘合性能。结果表明:在初始和蒸汽老化条件下,黄铜镀层钢丝帘线与胶料的粘合力随着铜含量的增大而下降;三相合金镀层中的钴可以抑制老化过程中脱锌的速度,因此蒸汽老化后,其粘合性能保持率高于黄铜镀层钢丝帘线。
The adhesion between steel cord with ternary alloy wire coating(TAWI) and cobalt-free compound was compared with that between brass coated steel cord and cobalt-containing compound. The results showed that under the initial and steam aging conditions,the adhesive force between brass-coated steel cord and rubber compound decreased with the increasing of the copper content. The cobalt in TAWI could lower the dezincification rate,and so,after steam aging,the adhesive retention rate of TAWI steel cord was higher than brass coated steel cord.
出处
《轮胎工业》
CAS
2018年第2期117-120,共4页
Tire Industry
关键词
钢丝帘线
黄铜镀层
铜含量
三相合金镀层
粘合力
steel cord
brass plating
copper content
ternary alloy wire coating
adhesive force