Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673 K were investigated. The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desorption (TPD) of ammonia. The structure of the samples was characterized by XRD, and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy (SEM). The XRD results show that the modified samples have no novel crystalline phase, indicating a high dispersion of phosphorus and boron species. After treatment, the microporous volume and surface area of the samples markedly decrease, implying the blockage of the channel. The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type I and IV, and all hysteresis loops resemble the H4-type in the IUPAC classification. The total acidity of the modified samples, determined by pyridine adsorption IR and TPD of ammonia, decreases in contrast to that of the parent HZSM-5. The conversion of n-heptane over P and B steam-modified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.
Physicochemical and catalytic properties of phosphorus and boron modified HZSM-5 zeolites treated with 100% steam at 673 K were investigated. The acidity and distribution of acidic sites were studied by infrared spectroscopy using pyridine as probe molecule and temperature programmed desorption (TPD) of ammonia. The structure of the samples was characterized by XRD, and the textural properties of the catalysts were determined by nitrogen isothermal adsorption-desorption measurements and scanning electron microscopy (SEM). The XRD results show that the modified samples have no novel crystalline phase, indicating a high dispersion of phosphorus and boron species. After treatment, the microporous volume and surface area of the samples markedly decrease, implying the blockage of the channel. The nitrogen adsorption-desorption measurements suggest that the isothermal type of all samples is a combination of isothermal type I and IV, and all hysteresis loops resemble the H4-type in the IUPAC classification. The total acidity of the modified samples, determined by pyridine adsorption IR and TPD of ammonia, decreases in contrast to that of the parent HZSM-5. The conversion of n-heptane over P and B steam-modified HZSM-5 is higher than that of P and B-modified HZSM-5 zeolites but lower than that of the parent HZSM-5.
基金
Financial support from Catalytic Key Laboratory of China Petroleum and Natural Gas Group Corpo- ration (University of Petroleum) was greatly appre- ciated. We thank the National Science Foundation Committee for Grant NSFC 20233030.