针对 16Mn系列高强度低合金钢连铸坯轧制中厚板生产中 ,因表面微裂纹钢板报废率高的问题 ,在采用镀层结晶器的基础上 。
In order to decrease the surface micro-crack defects occurred on the 16Mn plates rolled from continuously cast slabs using plated moulds, the relationship between crystallization performance of mould fluxes and rejection rate of plates due to surface micro-crack defects was studied in detail.