Titanium dioxide Nanotubes(TNTs) prepared by electroless deposition have been annealed at air ambient and low temperature. As a result, the anatase/rutile phase composition of the TNTs can be tailored to the needs of later applications. Nanotubes with anatase/rutile mixed phase ratio of 4:1 have been produced in this report and further examined for their photocatalytical behavior. The photocatalytical properties of the TNTs have been observed by degradation of methylene-blue in aqueous solution under low power UV-light irradiation. The results shown in this report are based on the synergetic effect between rutile and anatase,which results in the mixed phase TiO 2 nanotubes having enhanced photocatalytical properties.
Titanium dioxide Nanotubes(TNTs) prepared by electroless deposition have been annealed at air ambient and low temperature. As a result, the anatase/rutile phase composition of the TNTs can be tailored to the needs of later applications. Nanotubes with anatase/rutile mixed phase ratio of 4:1 have been produced in this report and further examined for their photocatalytical behavior. The photocatalytical properties of the TNTs have been observed by degradation of methylene-blue in aqueous solution under low power UV-light irradiation. The results shown in this report are based on the synergetic effect between rutile and anatase,which results in the mixed phase TiO 2 nanotubes having enhanced photocatalytical properties.