摘要
Three-dimensional(3D) flower-like Co–Al layered double hydroxide(Co–Al-LDH) architectures composed of atomically thin nanosheets were successfully synthesized via a hydrothermal method in a mixed solvent of water and butyl alcohol. Owing to the unique hierarchical structure and modification by butyl alcohol, the electrochemical stability and the charge/mass transport of the Co–Al-LDHs was improved. When used in supercapacitors, the obtained Co–Al-LDHs deliver a high specific capacitance of 838 Fg^(-1) at a current density of 1 Ag^(-1)and excellent rate performance(753 Fg^(-1) at 30 Ag^(-1) and 677 Fg^(-1) at 100 Ag^(-1)), as well as excellent cycling stability with 95% retention of the initial capacitance even after 20,000 cycles at a current density of 5 Ag^(-1). This work provides a promising alternative strategy to enhance the electrochemical properties of supercapacitors.
Three-dimensional(3D) flower-like Co–Al layered double hydroxide(Co–Al-LDH) architectures composed of atomically thin nanosheets were successfully synthesized via a hydrothermal method in a mixed solvent of water and butyl alcohol. Owing to the unique hierarchical structure and modification by butyl alcohol, the electrochemical stability and the charge/mass transport of the Co–Al-LDHs was improved. When used in supercapacitors, the obtained Co–Al-LDHs deliver a high specific capacitance of 838 Fg^(-1) at a current density of 1 Ag^(-1)and excellent rate performance(753 Fg^(-1) at 30 Ag^(-1) and 677 Fg^(-1) at 100 Ag^(-1)), as well as excellent cycling stability with 95% retention of the initial capacitance even after 20,000 cycles at a current density of 5 Ag^(-1). This work provides a promising alternative strategy to enhance the electrochemical properties of supercapacitors.
基金
supported by the National Basic Research Program of China(2014CB239702)
Research project of environmental protection in Jiangsu province(2016060)
Science and Technology Commission of Shanghai Municipality(14DZ2250800)