In this study, hydrothermal carbonization(HTC)was applied for surface functionalization of carbon nanotubes(CNTs) in the presence of glucose and urea. The HTC process allowed the deposition of thin nitrogen-doped carbon layers on the surface of the CNTs. By controlling the ratio of glucose to urea, nitrogen contents of up to 1.7 wt%were achieved. The nitrogen-doped carbon nanotube-supported Pd catalysts exhibited superior electrochemical activity for ethanol oxidation relative to the pristine CNTs.Importantly, a 1.5-fold increase in the specific activity was observed for the Pd/HTC-N1.67%CNTs relative to the catalyst without nitrogen doping(Pd/HTC-CNTs). Furtherexperiments indicated that the introduction of nitrogen species on the surface of the CNTs improved the Pd(0)loading and increased the binding energy.
In this study, hydrothermal carbonization(HTC)was applied for surface functionalization of carbon nanotubes(CNTs) in the presence of glucose and urea. The HTC process allowed the deposition of thin nitrogen-doped carbon layers on the surface of the CNTs. By controlling the ratio of glucose to urea, nitrogen contents of up to 1.7 wt%were achieved. The nitrogen-doped carbon nanotube-supported Pd catalysts exhibited superior electrochemical activity for ethanol oxidation relative to the pristine CNTs.Importantly, a 1.5-fold increase in the specific activity was observed for the Pd/HTC-N1.67%CNTs relative to the catalyst without nitrogen doping(Pd/HTC-CNTs). Furtherexperiments indicated that the introduction of nitrogen species on the surface of the CNTs improved the Pd(0)loading and increased the binding energy.
基金
financial support of the National Natural Science Foundation of China(Nos.51672045 and 11374053)
Key Program of Universityindustry Collaboration from Science and Technology Department of Fujian Province(No.2015H6009)