The relation between stacking fault overlap and martensitic nucleation in Fe-17Mn-10Cr-5Si-4Ni alloy was studied.The arrayed structure of dislocations and characteristics ofε-martensite formation under stress were in-situ observed by TEM.The results reveal thatε-martensite nucleates at the top of stacking faults overlapped band,where the ordered arrayed structure of Shockley partial dislocations exists.External stress promotesε-martensitic nucleation ability because of accelerated ordering of Shockley partial dislocations in stacking faults overlapped band.
The relation between stacking fault overlap and martensitic nucleation in Fe-17Mn-10Cr-5Si-4Ni alloy was studied.The arrayed structure of dislocations and characteristics ofε-martensite formation under stress were in-situ observed by TEM.The results reveal thatε-martensite nucleates at the top of stacking faults overlapped band,where the ordered arrayed structure of Shockley partial dislocations exists.External stress promotesε-martensitic nucleation ability because of accelerated ordering of Shockley partial dislocations in stacking faults overlapped band.
基金
Item Sponsored by National Natural Science Foundation of China(59801005)