摘要
Two types of carbides M23C6 and M7C3 precipitate orderly as carbon concentration in a high Cr-Ni austenitic steel increases during carburization process. The mathematical model that describes diffusion of carbon and the precipitation of M23C6 and M7C3 has been studied. A criterion to judge when the transformation of M23C6 to M7C3 is over and M7C3 precipitates directly has been given in simulated calculation. By applying the model, the carburization of HK40 steel has been calculated by means of finite difference computation techniques. The pack carburization tests for the HK40 steel have been carried out at 1273 K. The comparison between the experimental and the calculated results show acceptable agreement.
Two types of carbides M23C6 and M7C3 precipitate orderly as carbon concentration in a high Cr-Ni austenitic steel increases during carburization process. The mathematical model that describes diffusion of carbon and the precipitation of M23C6 and M7C3 has been studied. A criterion to judge when the transformation of M23C6 to M7C3 is over and M7C3 precipitates directly has been given in simulated calculation. By applying the model, the carburization of HK40 steel has been calculated by means of finite difference computation techniques. The pack carburization tests for the HK40 steel have been carried out at 1273 K. The comparison between the experimental and the calculated results show acceptable agreement.
基金
This work was supported by the National Natural Science Foundation of China under grant No.50071016.