The influences of alloying elements W, Mo, Cr, and Nb on retained ft phase in 47AI based near 7-TiAI alloys have been studied. The results reveal that the amount of retained β phase is increased by the addition of Cr, Mo, W in rising rank, although the distribution of β phase in Cr-bearing alloys is different from that of Mo- or W-bearing alloys. For Nb-doped alloys, no retained ft was found even when 5 at. pct Nb was added. The as-cast microstructural features and the distribution of the b phase in the different alloy families were compared and interpreted in terms of the different segregation behaviour of these elements in Ti.
The influences of alloying elements W, Mo, Cr, and Nb on retained ft phase in 47AI based near 7-TiAI alloys have been studied. The results reveal that the amount of retained β phase is increased by the addition of Cr, Mo, W in rising rank, although the distribution of β phase in Cr-bearing alloys is different from that of Mo- or W-bearing alloys. For Nb-doped alloys, no retained ft was found even when 5 at. pct Nb was added. The as-cast microstructural features and the distribution of the b phase in the different alloy families were compared and interpreted in terms of the different segregation behaviour of these elements in Ti.